Influence of activation conditions on the compressive strength, microstructure, and reaction products of sugarcane bagasse ash cements
DOI:
https://doi.org/10.5377/nexo.v35i02.14624Keywords:
alkali-activated cement, sugarcane bagasse ash, calcium aluminate cement, compressive strength, microstructure, reaction productsAbstract
Pastes of sugarcane bagasse ash (SCBA) and calcium aluminate cement (CAC) were activated with sodium silicate solutions, varying the SCBA content (80-95 wt.%), the SiO2/Na2O ratio (8-14 wt.% respect to the weight of SCBA), and the curing temperature (20 and 40 ºC or 100 and 200 ºC). 28 days-compressive strength between 5-20 MPa were obtained. The results are close to the reported in the literature for pastes of SCBA/metakaolin. Overall, it was observed that the compressive strength decreased with the increase in the curing temperature from 100 to 200 ºC. The gain in the compressive strength was attributed to the formation of a dense matrix of amorphous reaction products such as C-S-H, N-A-S-H, C-A-S-H, or silica gel. Our results stress the feasibility to use higher contents of sugarcane bagasse ash to obtain alkali-activated cement with compressive strengths up to 20 MPa. Further work is currently underway to identify the effect of some variables on the compressive strength of composites.
Downloads
303
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2022 Universidad Nacional de Ingeniería
![Creative Commons License](http://i.creativecommons.org/l/by/4.0/88x31.png)
This work is licensed under a Creative Commons Attribution 4.0 International License.
The authors who publish in Nexo Scientific Journal agree to the following terms:
- Authors retain the copyright and grant the journal the right of the first publication under the license Creative Commons Attribution License, which allows others to share the work with a recognition of the authorship of the work and the initial publication in Nexo Scientific Journal.
- Authors may separately establish additional agreements for the non-exclusive distribution of the version of the work published in the journal (for example, in an institutional repository or a book), with the recognition of the initial publication in Nexo Scientific Journal.
- Authors are allowed and encouraged to disseminate their works electronically (for example, in institutional repositories or in their own website) before and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published works.